PBT GF30 Reinforced Flame Retardant Glass Fiber Reinforced 30% Composite PBT Plastic Particles

• Feature: Photodegradable
• CAS No.: 24968-12-5
• Formula: (C12h12o4)N
• Model NO.: PBT GF30
• EINECS: /
• Material: Polybutylene Terephthalate/PBT
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Model. No: PBT GF30
• Sample: Free
• Grade: Injection
• Delivery Time: 7~15days
• Transport Package: Bag
• Specification: 25Kgs/Bag
• Origin: China
• HS Code: 3907991090
• Production Capacity: 1500tons/Month

Product Description

Product Description

It is a thermoplastic (semi-)crystalline polymer, and a type of polyester. PBT resists solvents, shrinks very little during forming, is mechanically strong, is heat-resistant up to 150 °C (or 200 °C with glass-fibre reinforcement), and can be treated with flame retardants to make it noncombustible.

Product Parameters

Property Rheological properties	Test Condition	Unit	Standard	guide value
C Melt volume-flow rate	260 °C; 2.16 kg	cm³/(10 min)	ISO 1133-1	18
C Molding shrinkage, parallel	60x60x2; 250 °C / WZ 80° C; 600 bar	%	ISO 294-4	0.5
C Molding shrinkage, transverse	60x60x2; 250 °C / WZ 80° C; 600 bar	%	ISO 294-4	1.2
Post- shrinkage, parallel	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Post- shrinkage, transverse	60x60x2; 120 °C; 4 h	%	ISO 294-4	0.1
Mechanical properties (23 °C/50 % r. h.)
C Tensile modulus	1 mm/min	MPa	ISO 527-1,-2	7500
C Tensile Stress at break	5 mm/min	MPa	ISO 527-1,-2	125
C Tensile Strain at break	5 mm/min	%	ISO 527-1,-2	2.8
C Tensile creep modulus	1 h	MPa	ISO 899-1	7300
C Tensile creep modulus	1000 h	MPa	ISO 899-1	6900
C Charpy impact strength	23 °C	kJ/m²	ISO 179-1eU	45
C Charpy impact strength	-30 °C	kJ/m²	ISO 179-1eU	40
C Charpy notched impact strength	23 °C	kJ/m²	ISO 179-1eA	< 10
C Charpy notched impact strength	-30 °C	kJ/m²	ISO 179-1eA	< 10
Izod impact strength	23 °C	kJ/m²	ISO 180-1U	40
Izod impact strength	-30 °C	kJ/m²	ISO 180-1U	35
Izod notched impact strength	-30 °C	kJ/m²	ISO 180-1A	< 10
Izod notched impact strength	-40 °C	kJ/m²	ISO 180-1A	< 10
Flexural modulus	2 mm/min	MPa	ISO 178-A	7200
Flexural strength	2 mm/min	MPa	ISO 178-A	185
Flexural strain at flexural strength	2 mm/min	%	ISO 178-A	3.2
Ball indentation hardness		N/mm²	ISO 2039-1	200
Thermal properties
C Melting temperature	10 °C/min	°C	ISO 11357-1,-3	225
C Temperature of deflection under load	1.80 MPa	°C	ISO 75-1,-2	200
C Temperature of deflection under load	0.45 MPa	°C	ISO 75-1,-2	220
Vicat softening temperature	50 N; 120 °C/h	°C	ISO 306	210
C Coefficient of linear thermal expansion, parallel	23 to 55 °C	10-4/K	ISO 11359-1,-2	0.3
C Coefficient of linear thermal expansion, transverse	23 to 55 °C	10-4/K	ISO 11359-1,-2	1.0
C Burning behavior UL 94	1.5 mm	Class	UL 94	V-0
C Burning behavior UL 94	1.00 mm	Class	UL 94	V-0
C Burning behavior UL 94-5V	3.5 mm	Class	UL 94	5VA
C Oxygen index	Method A	%	ISO 4589-2	32
Thermal conductivity	23 °C	W/(m·K)	ISO 8302	0.23