Carbon Content: | High-Carbon |
---|---|
Customization: | Yes |
Expansion Ratio: | >150ml/g |
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
RP | HP | UHP |
Electrode: Bulk Density≥ 1.56g/cm3 Specific Resistivity≤ 8.5μm Bending Strength≥ 10.0MPa Elastic Modulus≤ 9.3GPa Thermal Expansion Coefficient≤ 2.7x10 -6/°C Ash≤ 0.5% Nipple: Bulk Density≥ 1.68g/cm3 Specific Resistivity≤ 7.0μm Bending Strength≥ 14.0MPa Elastic Modulus≤ 13.7GPa Thermal Expansion Coefficient≤ 2.5 x10 -6/°C Ash≤ 0.5% |
Electrode: Bulk Density≥ 1.65g/cm3 Specific Resistivity≤ 6.5μm Bending Strength≥ 12.0MPa Elastic Modulus≤ 10.0GPa Thermal Expansion Coefficient≤ 2.2x10 -6/°C Ash≤ 0.3% Nipple: Bulk Density≥ 1.74g/cm3 Specific Resistivity≤ 5.5μm Bending Strength≥ 16.0MPa Elastic Modulus≤ 14.0GPa Thermal Expansion Coefficient≤ 2.0 x10 -6/°C Ash≤ 0.3% |
Electrode: Bulk Density≥ 1.68g/cm3 Specific Resistivity≤ 5.8μm Bending Strength≥ 16.0MPa Elastic Modulus≤ 14.0GPa Thermal Expansion Coefficient≤ 1.9x10 -6/°C Ash≤ 0.2% Nipple: Bulk Density≥ 1.76g/cm3 Specific Resistivity≤ 4.5μm Bending Strength≥ 18.0MPa Elastic Modulus≤ 16.0GPa Thermal Expansion Coefficient≤ 1.4 x10 -6/°C Ash≤ 0.2% |
Category | No. | Specifications | |
Diameter (mm) | Length (mm) | ||
Ultra high power graphite electrode | 1 | 300 | 1800 |
2 | 350 | 1800 | |
3 | 400 | 2200 | |
4 | 450 | 1800 | |
5 | 500 | 2200 | |
6 | 550 | 2300 | |
7 | 600 | 2400 | |
8 | 700 | 2700 |
Technical Properties of Ultra High Power Graphite Electrodes and nipple | ||||||||
Item | Classification | Unit | NominalDiameter (mm) | |||||
300-400 | 450-500 | 550-700 | ||||||
Electric Resistivuty(<=) | Elatrode | μΩ.m | 6.2 | 6.2 | 6.3 | |||
Nipple | 5.0 | 5.0 | 4.5 | |||||
Bending strength(>=) | Elatrode | Mpa | 10.5 | 10.5 | 11.0 | |||
Nipple | 18.0 | 18.0 | 20.0 | |||||
Elastic moduluc(<=) | Elatrode | Gpa | 14.0 | 14.0 | 14.0 | |||
Nipple | 18.0 | 18.0 | 22.0 | |||||
Bulk density(>=) | Elatrode | g/cm3 | 1.66 | 1.66 | 1.66 | |||
Nipple | 1.75 | 1.75 | 1.75 | |||||
CTE(<=) | Elatrode | X10-6/ºC | 1.5 | 1.5 | 1.4 | |||
Nipple | 1.4 | 1.4 | 1.2 | |||||
Ash(<=) | % | 0.3 | 0.3 | 0.5 | ||||
Note: Ash content and thermal expansion coefficient are parameter indicators |