High Quality Virgin Polyethylene Resin LDPE-Pem1850A Granules High Transparent Blow Molded

• Feature: Oxidative Degradable
• CAS No.: 9002-88-4
• Formula: (C2h4)N
• EINECS: 200-815-3
• Material: Low Density Polyethylene/LDPE
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Blow Molding
• Color: Lucency
• Melting Point: 85-110c
• Form: 3-5 mm Granules
• Water Solubility: Insoluble
• Sample: Free
• Delivery Time: 7~15days
• Transport Package: Bag
• Specification: 25Kgs/Bag
• Origin: China
• HS Code: 3901100090
• Production Capacity: 1500tons/Month

Product Description

Low density polyethylene, also known as high pressure polyethylene (LDPE), is the lightest variety of polyethylene resin, which is milky, tasteless, odorless, non-toxic, waxy particles with a dull surface. It has good softness, extensibility, electrical insulation, transparency, ease of processing and certain permeability. Its chemical stability is good, alkali resistance, resistance to general organic solvents.
Low density polyethylene has the following characteristics:
(1) The film is slightly opal transparent and soft. The strength is smaller than high-density polyethylene, and the impact strength is larger than high-density polyethylene.
(2) Cold resistance, low temperature resistance and high temperature resistance. The thicker film can withstand the sterilization process of 90ºC hot water immersion.
(3) moisture resistance is better, chemical performance is stable, insoluble in general solvents.
(4) It has large breathability, so when it is used as a food packaging that is easily oxidized, the storage period of its contents should not be too long.
(5) The oil resistance is poor, and the product can be slowly dissolved. When packaging food containing fat, it will make the food appear rancid after long storage.
(6) Long-term exposure to ultraviolet light and heat will age, affecting its physical properties and dielectric properties.
(7) The melting point is 110~115 ° C, the processing temperature is 150~210 ° C, if in the inert gas, the temperature can reach 300 ° C is still stable. However, contact between melt and oxygen is easy to degrade.

LDPE Injection Grade

Tests	Value	Unit
Melt Flow Rate   (MFR)	15	g/10min
Density	0.922	g/cm3
Tensile Yield   Strength	7	Mpa
Elongation at Break	75	%
Wien Softening   Point	85	°C

 
 LDPE Film Grade

Tests	Value	Unit
Melt Flow Rate   (MFR)	2	g/10min
Density	0.9225	g/cm3
Tensile Strength	9	Mpa
Elongation at Break	500	%
Fish eye   max(0.3-2mm)	30	n/1200cm2
Stripes	20	cm/20m3

Appliction
1.Fiber ( Carpet, Textils, Upholstery, etc.)
2.Film ( shopping bags, casting film, multilayer film, etc.)
3.Blow Molding ( Medical & Cosmetic container, Lubricant & Paint container, etc)
4.Extrusion Molding ( Sheet, Pipe, Wire & Cable, etc.)
5.Injection Molding ( Automotive, Electronic, Construction, House wares, Furniture,Toys, etc.)
Packaging&Shipping
25kg/ carton or 25kg/bag, or per your requirement

25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container