Hot Sale E503105vc T2 PVC Compounds for Automotive Wire

• Feature: Photodegradable
• CAS No.: 9002-86-2
• Formula: (CH2-Chcl)N
• Model NO.: E503105VC PVC
• EINECS: /
• Material: Polyvinyl Chloride/PVC
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film Pressure
• Color: White
• Model.No.: PVC Ry-E504105vc
• Sample: Free
• Delivery Time: 7~15days
• Grade: High Quality
• Transport Package: Carton
• Specification: 25Kgs/Bag
• Origin: China
• HS Code: 3904109001

Product Description

Product Description
product name:Hot sale E503105VC  T2 PVC Compounds for Automotive Wire
PVC resin is the most widely raw material used in plastic production. It has good chemical stability corrosion resistance and water resistance. It can be dissolved in ace-tones , hydrochloric ether, ester and some alcohol .
The PVC Resins are polymerized by suspension process, their appearance being in white powder form. They are essential materials for preparing PVC compounds. By adding blending agents and employing different techniques, they can be made into rigid or non-rigid PVC products and are suppliable in a wide range of transparent, translucent, and opaque colours.
Our PVC Resins are distinguished for their insulating, moisture-proof, oil-resistant, acid-resistant, and alkali-resitant properties.
  

Application

  
 

Item No	Description					Application
RY-E50180VC	80ºC  insulation grade PVC Compounds for automotive thin- wall wires					Comply with JIS C3406, JASO D611-94,SAEJ1128 and similar standards
RY-E50290VC	90ºC Environmentally friendly insulation grade PVC Compounds for automotive wires					Apply for the thin-wall and  low-voltage cable insulation,  Comply with JASO D611standards. Small size wire can meet the ISO 6722 scratch resistance test
RY-E503105VC	105ºC insulation grade PVC Compounds for automotive thin -wall wires					Comply with DIN72551,VW60306-2005,LV112 and similar standards
RY-E504105VC	105ºC Environmentally friendly insulation grade PVC Compounds for automotive wires					Comply with German standard 105ºC grade, Franch standard T2 grade or National industry standard QVR-105 grade. meet the heat resistance requirements for  thin-wall automotive wire insulation.
RY-E505105VC	105ºC  Environmentally friendly insulation grade soft PVC Compounds for automotive wires					Apply for 105ºC grade automobile battery wire

 

 

Technical Properities:

 

No	Item	Unit	RY-E50180VC	RY-E50290VC	RY-E503105VC	RY-E504105VC	RY-E505105VC
1	Tensile Strength	MPa	≥18	≥16	≥18	≥16	≥16
2	Elongation at Break	%	≥200	≥150	≥250	≥150	≥180
3	Thermal Deformation	%	≤30	≤40	≤30	---	≤30
4	Impact Brittleness Temperature	ºC	-20	-20	-25	-20	-25
5	Thermal stability time at 200ºC	min	≥120	≥80	≥200	≥80	≥80
6	Volume Resistivity at 20ºC	Ω.m	≥1.0×10^11	≥1.0×10^11	≥1.0×10^12	≥1.0×10^11	≥1.0×10^11
7	Work Temperature	ºC	80	---	95±1	---	---
	Volume Resistivity at Work Temperature	Ω.m	≥1.0×10^8	---	≥1.0×10^8	---	---
8	Dielectric Strength	MV/m	---	≥20	---	≥20	---
9	Thermal Aging  Performance(IEC)	ºC× day	121×7	120×7	136×7	135×7	135×7
	Tensile Strength after Aging	MPa	---	≥16	---	≥16	≥16
	Retention Rate of Tensile Strength after Aging	%	≥85	≥75	≥80	≥75	≥75
	Elongation at Break after Aging	%	---	≥150	---	≥150	≥150
	Retention Rate of Elongation at Break after Aging	%	≥65	≥75	≥80	≥75	≥75
10	Thermal Aging  Performance(IEC)	ºCx day	---	---	---	125×10	---
	Tensile Strength after Aging	MPa	---	---	---	≥16	---
	Elongation at Break after Aging	%	---	---	---	≥150	---
	Mass Loss	mg/cm^2	---	---	---	2	---
11	Oil Resistant Test(IRM902oil,50ºCx24h)
	Change Rate of Tensile Strength	%	---	≤±25	---	≤±25	≤±25
	Change Rate of Elongation at Break	%	---	≤±25	---	≤±25	≤±25
12	Hardness	ShoreA	92±3	---	92±3	---	---

 

 


 